Certified material
Hot-dip galvanized steel sheets & coil
Total net weight · 8 coils
37,305 kg
Total gross weight
37,500 kg
Recorded results
Details by size
Chemical composition expressed × 1,000
0.60 MM × 1250 MM × COIL
G · Good
Weight
Net7,605 kg
Gross7,655 kg
Mechanical test
Hardness55.6 HRB
Yield point (YP)251 N/mm²
Tensile strength (TS)353 N/mm²
Elongation (EL)39%
Coating and traceability
Zinc coating182.8 g/m²
Heat No.2232352
Gloss T/B0.0% / 0.0%
Coating thickness T/B0 μm / 0 μm
Surface finishingChromate / dry
0.75 MM × 1250 MM × COIL
G · Good
Weight
Net14,550 kg
Gross14,600 kg
Mechanical test
Hardness57.2 HRB
Yield point (YP)250 N/mm²
Tensile strength (TS)352 N/mm²
Elongation (EL)41.9%
Coating and traceability
Zinc coating182.8 g/m²
Heat No.2232352
Gloss T/B0.0% / 0.0%
Coating thickness T/B0 μm / 0 μm
Surface finishingChromate / dry
1,00 MM × 1250 MM × COIL
G · Good
Weight
Net7,565 kg
Gross7,610 kg
Mechanical test
Hardness55.6 HRB
Yield point (YP)249 N/mm²
Tensile strength (TS)351 N/mm²
Elongation (EL)38.8%
Coating and traceability
Zinc coating182.2 g/m²
Heat No.2232352
Gloss T/B0.0% / 0.0%
Coating thickness T/B0 μm / 0 μm
Surface finishingChromate / dry
1,20 MM × 1250 MM × COIL
G · Good
Weight
Net7,585 kg
Gross7,635 kg
Mechanical test
Hardness55.6 HRB
Yield point (YP)249 N/mm²
Tensile strength (TS)351 N/mm²
Elongation (EL)38.8%
Coating and traceability
Zinc coating182.2 g/m²
Heat No.2232352
Gloss T/B0.0% / 0.0%
Coating thickness T/B0 μm / 0 μm
Surface finishingChromate / dry
Certification
Manufacturer's declaration
Document reference
Format information
Code and page
USS-G-0913-01 REV.2 · Page 1 / 1
Abbreviations, origin and format
T: top · B: back · G: good · GRS wt: gross wt
Made in Korea · A4 (210 × 297)
Direct access
QR for the English version
This code opens this page directly and is the one shown on the enhanced copy of the certificate.
Download QR code
View the original mill certificate
English transcription of the content visible on the certificate. Values, units and technical codes were preserved; blank fields were not completed.